Mn13 thin wear-resistant steel plate spot 
 Professional team, focused on steel, hard service! 
 Shanghai Steel Kai solemn promise: a penalty at ten! A penalty at ten! A penalty at ten! A penalty at ten! A penalty at ten! A penalty at ten! 
 Sincere service! Procurement of materials from our company, a round on each plate are each an original 100% guaranteed authentic, together with the material and the material corresponding to the book, please be assured co-operation with the Shanghai steel Kai! 
 ---------------------------------- 
 Kai Steel Co., Ltd Shanghai Steel (for many years specialized in all kinds of high-grade steel) 
 Spot a spot two groups of 021 -66630039 021 -56691522 -66630298 Fax :021 
 Business QQ: 327237499 / 969552363 / 1425895918 / 493783205 
 Business Manager: spot a spot two groups 15,900,718,360 18,964,196,422 Zhang Ting Shuai Dong 
 Official Website www.steelqi.com 
 Address: River Road, Baoshan District Shanghai, Lane 448 No. 1, 1402 (Baosteel No. 2 Gate 2 km) Welcome to the new and old customers to visit the first to make friends! Integrity first, customer first, to a grateful heart and a professional business knowledge to provide customers with comprehensive after sales service. 
 ---------------------------------- 
 Name of material: high manganese steel 
 Grade: Mn13 
 Standard: GB 5680-98 
 U.S. high-manganese steel standard AISI A128 Grade A 
 Japanese high-manganese steel standard JIS: SCMnH11 
 French high-manganese steel standard AFNOR: Z120Mn12 
 German high-manganese steel standard DIN / EN: X120Mn12 
 High-manganese steel standard 116Г13Ю the former Soviet Union 
 U.S. high-manganese steel standard ASTM: A128 
 China's high-manganese steel standard: GB 5680-98 MN13 
 Shanghai Steel Sales Tel :021 -56,691,522 Kai 
 MN13 1 * 1000 * 2000 (Baosteel) 1000 ° C water and tough treatment 
 MN13 1.5 * 1000 * 2000 (Baosteel) 1000 ° C water and tough treatment 
 MN13 2.0 * 1000 * 2000 (Baosteel) 1000 ° C water and tough treatment 
 Mn13 3 * 1000 * 2000 (Baosteel) 1000 ° C water and tough treatment 
 Mn13 4 * 2000 * 6000 (Baosteel) 1000 ° C water and tough treatment 
 Mn13 5 * 2000 * 6000 (Baosteel) 1000 ° C water and tough treatment 
 Mn13 6 * 2000 * 5800 (Baosteel) 1000 ° C water and tough treatment 
 Mn13 8 * 2160 * 5720 (Baosteel) 1000 ° C water and tough treatment 
 Mn13 10 * 1940 * 5480 (Baosteel) 1000 ° C water and tough treatment 
 Mn13 10 * 1970 * 4600 (Baosteel) 1000 ° C water and tough treatment 
 Mn13 10 * 2010 * 4340 (Baosteel) 1000 ° C water and tough treatment 
 Mn13 12 * 2000 * 6000 (Baosteel) 1000 ° C water and tough treatment 
 Mn13 12 * 1970 * 2220 (Baosteel) 1000 ° C water and tough treatment 
 Mn13 12 * 1980 * 5120 (Baosteel) 1000 ° C water and tough treatment 
 Mn13 12 * 2010 * 7480 (Baosteel) 1000 ° C water and tough treatment 
 Mn13 12 * 2030 * 7400 (Baosteel) 1000 ° C water and tough treatment 
 Mn13 12 * 2030 * 6000 (Baosteel) 1000 ° C water and tough treatment 
 Mn13 16 * 1000 * 2150 (Baosteel) 1000 ° C water and tough treatment 
 Mn13 16 * 1000 * 2010 (Baosteel) 1000 ° C water and tough treatment 
 Mn13 20 * 1930 * 4600 (Baosteel) 1000 ° C water and tough treatment 
 Mn13 20 * 2010 * 4340 (Baosteel) 1000 ° C water and tough treatment 

 Impact wear the best choice, a "strike hard" features, especially for the impact of abrasive wear and high stress crushed abrasion condition, commonly used in the manufacture of ball mill liner, hammer hammer crusher, jaw crusher jaw plate, cone crusher roll mortar wall, broken walls, excavator bucket teeth, bucket wall, railway turnouts, crawler tractors and tanks board impact, wear resistant castings. High-manganese steel is also used: bullet-proof steel, safe plate and so on. 

 Mn13 Features and application: 
 Mn13 used need to withstand impact, extrusion, material abrasion and other harsh working conditions, wear and tear damage to form the main part of the fracture and deformation. Wear is divided into three types: mutual contact between the surface of metal components and movement of friction and wear; other metal or non-metallic material impact on the abrasive wear of metal surfaces and the flowing gas or liquid contact with the metal caused by erosion. Abrasion wear resistance of steel depends on the material itself, while the wear of steel in different working conditions show different wear resistance, the material itself and working conditions between the two in order to determine their wear resistance. 
 Abrasion resistant steel and cast steel to austenitic manganese-based, under certain conditions the low alloy steel with appropriate heat treatment has good results, graphite is used for lubrication of the friction of steel working conditions. 
 Especially suitable for high wear-resistant manganese steel and high impact abrasive wear stress crushed abrasion condition, commonly used in the manufacture of ball mill liner, hammer hammer crusher, jaw crusher jaw plate, cone crusher roll mortar wall, broken Wall, excavator bucket teeth, bucket wall, railway turnouts, tractors and tank track shoes and other impact, abrasion resistance of castings. High-manganese steel is also used: bullet-proof steel, safe plate and so on. 
 High-manganese steel is a typical anti-wear steel, cast structure of austenite plus carbide. About 1000 ° C by water quenching 
 Treatment organizations into a single small amount of austenite or austenite plus carbide, but to improve toughness, so called tough water treatment. 
 The most important feature of high-manganese steel is in a strong impact, extrusion conditions, the surface hardening rapidly, so that the Department of mind remains austenitic good toughness and ductility, while hardening layer has good abrasion resistance. This is less than the other materials. However, the wear resistance of high-manganese steel have enough to form only in the hardening conditions to demonstrate its advantages, other cases are poor. 
 Mn13 chemical composition: 
 Carbon C: 1.10 ~ 1.50 
 Si Si: 0.30 ~ 1.00 
 Manganese Mn: 11.00 ~ 14.00 
 Sulfur S: ≤ 0.050 
 Phosphorus P: ≤ 0.090 

 MN13 physical properties: 
 Tensile σb (Mpa): 880 ~ 1130 
 Yield Re (Mpa): ≥ 410 
 Elongation δ (%): ≥ 40 
 Impact energy Akv (J): 124 (room temperature) 
 Hardness ≤ 229HB